1.JPE采用埃克森美孚化工的茂金属催化剂并运用高压法技术生产的产品.
2.用高强度及低析出量技术生产的茂金属聚乙烯弹性体("塑性体")
3.最适合低温热封和改性剂使用.
|
产品名称
|
KF260T
|
KF270
|
KF271
|
KF283
|
KF360T
|
KF370
|
KF380
|
KC572SC
|
KC573
|
KC580S
|
KC581
|
KS240T
|
KS340T
|
KF261T
|
KS560T
|
KJ640T
|
KJ740T
|
|
熔指g/10min
|
2.0
|
2.0
|
2.4
|
2.5
|
3.5
|
3.5
|
4.0
|
17.5
|
15.0
|
10.5
|
10.5
|
2.2
|
3.5
|
2.2
|
16.5
|
30
|
50
|
|
密度g/cm³
|
0.901
|
0.907
|
0.913
|
0.921
|
0.898
|
0.905
|
0.918
|
0.900
|
0.910
|
0.920
|
0.919
|
0.880
|
0.880
|
0.898
|
0.898
|
0.880
|
0.880
|
|
熔点℃
|
93
|
100
|
102
|
108
|
90
|
97
|
106
|
92
|
102
|
109
|
109
|
60
|
60
|
90
|
90
|
58
|
58
|
|
拉伸撕裂强度MPa
|
6.5
|
7.2
|
9.4
|
12
|
5.3
|
6.8
|
11
|
5.9
|
8.0
|
9.1
|
9.1
|
3.2
|
3.2
|
5.7
|
4.8
|
2.9
|
2.9
|
|
拉伸断裂强度MPa
|
42
|
42
|
40
|
39
|
41
|
41
|
39
|
41
|
22
|
21
|
21
|
38
|
36
|
42
|
30
|
15
|
10
|
|
拉伸伸长率%
|
650
|
680
|
700
|
730
|
670
|
710
|
750
|
900
|
850
|
760
|
760
|
680
|
720
|
650
|
840
|
1060
|
1060
|
|
弯曲模量MPa
|
62
|
71
|
120
|
235
|
53
|
57
|
205
|
60
|
110
|
167
|
167
|
23
|
23
|
52
|
52
|
22
|
21
|
|
硬度(SHORE D)
|
43
|
48
|
55
|
57
|
41
|
46
|
56
|
41
|
45
|
50
|
50
|
31
|
31
|
41
|
40
|
26
|
26
|
|
硬度(SHORE A)
|
93
|
94
|
97
|
99
|
90
|
94
|
99
|
91
|
97
|
98
|
98
|
85
|
85
|
90
|
88
|
84
|
84
|
|
软化点℃
|
81
|
88
|
98
|
106
|
76
|
86
|
105
|
75
|
83
|
100
|
100
|
48
|
48
|
76
|
68
|
43
|
42
|
|
脆化温度℃
|
<-70
|
<-70
|
<-70
|
<-70
|
<-70
|
<-70
|
<-70
|
<-70
|
<-70
|
<-70
|
<-70
|
<-70
|
<-70
|
<-70
|
<-70
|
<-70
|
<-70
|
|
抗环境应力开裂 HRS
|
>1000
|
>1000
|
>1000
|
>1000
|
>1000
|
>1000
|
>1000
|
>1000
|
>1000
|
>1000
|
>1000
|
>1000
|
>1000
|
>1000
|
>1000
|
>1000
|
>1000
|
|
应用
|
吹膜
|
流延膜
|
挤出,注塑，涂覆
|
挤出,注塑，涂覆
|